Battery Separator Tissue

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Jiangsu
Validity to:
Long-term effective
Last update:
2018-06-18 09:08
Browse the number:
435

Send an inquiries

Company Profile

Nanjing EFG Co.,Ltd

By certification [File Integrity]

Contact：njfeige(Mr.)

Email：

Telephone：

Phone：

Area：Jiangsu

Address：Building 9, Cuiping International square, No. 20 Jiangjun Ave., Nanjing, China

Website：http://www.nanjingefg.com/ http://njfeige.hengshuiyt.com/

Product Details

Battery Separator Tissue
Battery separator tissue is produced with glass fiber and features high area weight, low DC mass resistivity, high absorption capacity, good acid resistance, low content of deoxidized KM-nO4 organic substance and low impurity as well as proper stiffness, smooth surface and uniform thickness. Using this fiberglass tissue as the separator, the compound lead acid battery has the advantages of low resistivity, high porosity and large capacity, better mechanical strength and vibration resistance. The battery fixed up with this type of separator plates has stronger starting power and longer service lifetime, therefore it has become a trend to replace the traditional battery separator plate with this fiberglass one.

Technical Data

Item	Unite	Specification
		S-BT0.3	S-BT0.4	S-BT0.5	S-BT0.6
Thickness	mm	0.3±0.03	0.4±0.03	0.5±0.04	0.6±0.04
Binder Content	%	＜20
Tensile Strength MD	N/5cm	≥60	≥80	≥100	≥120
Acid resistance in 15 minutes	%	≤2
Acid resistance in 72 hours	%	≤3
Thickness Variation	%	≤5
Wet Out	S	≤100	≤25	≤10	≤10
Original State Content of KMnO4 C(1/5KMnO4)=0.01/L	ml/g	≤15
CL Content	%	≤0.003
Fe Content	%	≤0.005
Mn Content	%	≤0.003
Roll Width	mm	1000±5

http://www.nanjingefg.com/